Investigation of the correlation between dielectric function, thickness and morphology of nano-granular ZnO very thin films - Université de technologie de Troyes Accéder directement au contenu
Article Dans Une Revue Thin Solid Films Année : 2015

Investigation of the correlation between dielectric function, thickness and morphology of nano-granular ZnO very thin films

Résumé

Thin nano-granular ZnO layers were prepared using a sol–gel synthesis and spin-coating deposition process with a thickness ranging between 20 and 120 nm. The complex dielectric function (ϵ) of the ZnO film was determined from spectroscopic ellipsometry measurements. Up to a critical thickness close to 60 nm, the magnitude of both the real and the imaginary parts of ϵ rapidly increases and then slowly tends to values closer to the bulk ZnO material. This trend suggests a drastic change in the film porosity at both sides of this critical thickness, due to the pre-heating and post-crystallization processes, as confirmed by additional characterization of the structure and the morphology of the ZnO films.
Fichier non déposé

Dates et versions

hal-02374069 , version 1 (21-11-2019)

Identifiants

Citer

Mickaël Gilliot, Aomar Hadjadj, Jérôme Martin. Investigation of the correlation between dielectric function, thickness and morphology of nano-granular ZnO very thin films. Thin Solid Films, 2015, 597, pp.65-69. ⟨10.1016/j.tsf.2015.11.035⟩. ⟨hal-02374069⟩

Collections

CNRS URCA LISM UTT
29 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More