Integrated Freestanding Two-dimensional Transition Metal Dichalcogenides

Abstract : his paper reports on the integration of freestanding transition metal dichalcogenides (TMDs). Monolayer (1‐L) MoS2, WS2, and WSe2 as representative TMDs are transferred on ZnO nanorods (NRs), used here as nanostructured substrates. The photoluminescence (PL) spectra of 1‐L TMDs on NRs show a giant PL intensity enhancement, compared with those of 1‐L TMDs on SiO2. The strong increases in Raman and PL intensities, along with the characteristic peak shifts, confirm the absence of stress in the TMDs on NRs. In depth analysis of the PL emission also reveals that the ratio between the exciton and trion peak intensity is almost not modified after transfer. The latter shows that the effect of charge transfer between the 1‐L TMDs and ZnO NRs is here negligible. Furthermore, confocal PL and Raman spectroscopy reveal a fairly consistent distribution of PL and Raman intensities. These observations are in agreement with a very limited points contact between the support and the 1‐L TMDs. The entire process reported here is scalable and may pave the way for the development of very efficient ultrathin optoelectronics.
Complete list of metadatas

https://hal-utt.archives-ouvertes.fr/hal-02364310
Contributor : Daniel Gavrysiak <>
Submitted on : Thursday, November 14, 2019 - 7:13:30 PM
Last modification on : Friday, November 15, 2019 - 1:36:54 AM

Identifiers

Collections

CNRS | P2MN | UTT

Citation

Hyun Jeong, Hye Min Oh, Anisha Gokarna, Hyun Kim, Seok Joon Yun, et al.. Integrated Freestanding Two-dimensional Transition Metal Dichalcogenides. Advanced Materials, Wiley-VCH Verlag, 2017, 29 (18), pp.1700308. ⟨10.1002/adma.201700308⟩. ⟨hal-02364310⟩

Share

Metrics

Record views

50